Low temperature ASTM A333 GR. 2 Carbon Steel Line Pipe, A333 Gr.2 Welded Pipe, ASME SA333 Grade 2 Schedule 40 Pipe exporter in India

ASTM A333 grade 1 is constructed from carbon-based alloy for low temperature service. The chemical composition of the A333 carbon steel pipe includes – manganese, phosphorus and sulphur. The tensile strength and yield strength for the A333 gr b pipe is variable among its grades. For example, the tensile strength is 380 MPa and yield strength is 205 MPa for grade 1. The tensile strength is 450 MPa and yield strength is 240 MPa for grade 3. While the tensile strength is 415 MPa and yield strength is 240 MPa for ASTM A333 grade 1 pipe schedule. The pipes made from SA333 gr 1 material are meant for low temperature applications. The A333 grade 1 pipe is available in either welded, ERW, CDW, fabricated or seamless type. While producing welded pipes, it is not necessary to add filler metals during the operation. These carbon steel A333 grade 1 pipes are surface treated. The pipe ends of the A333 Gr 1 seamless pipe could be bevelled, plain ended or threaded, depending on the requirement of the buyer.

Some of the surface treatments include a coating or finishing by Oil-dip, Phosphating, Varnish, Passivation or Shot Blasting. They could also be anodized or finished polish. The treatment gives the surface of the A333 gr 1 smls pipe a smooth and flawless appearance. ASTM A333 grade 1 pipe can be conventionally formed, cold-worked and welded. The A333 grade 1 pipe can be hot worked, but they can’t be hot worked below 1500 degrees F. The ASTM A333 grade 1 pipe equivalent pipe is used in the transportation of Chemical, Water and Gas.  SA333 gr1 pipe finds application in building or construction work, where they are used to deliver concrete pumps. We are one of the oldest A333 grade 1 pipe manufacturer.

ASTM A333 Grade 1 Pipe Specifications

S355 is a non-alloy European standard (EN 10025-2) structural steel, most commonly used after S235 where more strength is needed. It got great weld ability and machinability, let us see more mechanical details of this steel.

S355 Yield Strength

S355 is named based on it's minimum yield strength of 355 Mpa (N/mm2), However the yield strength reduces when you go up in thickness above 16 mm for flat products & hollow sections

Here is the table showing reduction in yield strength based on thickness
Up to 16 mm - 355 Mpa
16 mm < t  ≤ 40 mm -  345 Mpa
40 mm < t  ≤ 63 mm -  335 Mpa
63 mm < t  ≤ 80 mm -  325 Mpa
80 mm < t  ≤ 100 mm -  315 Mpa
100 mm < t  ≤ 150 mm -  295 Mpa

S355 Tensile Strength

S355 ultimate tensile strength ranges also varies based on thickness.
Up to 3 mm - 510 Mpa to 680 Mpa
3 mm < t  ≤ 100 mm -  470 Mpa to 630 Mpa
100 mm < t  ≤ 150 mm -  450 Mpa to 600 Mpa

S355 Density

Density of S355 is 7850 kg/m3 like all other mild steel

S355 Hardness (Brinell Hardness - HB)

Hardness for S355 J2 ranges from 146 HB to 187 HB

S355 Young's Modulus

S355 Youngs's Modulus is 190 to 210 Gpa, in a conservative design go for 190 Gpa

Chemical Composition of ASTM A335 Seamless Pipes:

• Carbon - 0.15% max
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.50%
• Chromium - 4.00% - 6.00%
• Molybdenum - 0.45% - 0.65%

 

 

 

 

 

 

ASTM a106 grade A has the lowest strength of the three grades but can still be useful for many applications. A106 grade A is useful because many clients will not need a pipe that is that heavy like grade B and C so they will choose grade A because it is affordable but offers excellent quality when dealing with transporting high-temperature gases or fluids. ASTM a106 grade A can be cut or shaped to a client’s request which will be convenient for the client when using the pipe for the application needed. Grade A has the lowest amount of carbon percentage which is usually around 0.25%. This shows how the strength of the pipe is lower than the other grades.

 

 

 

Carbon Steel Seamless Pipe

Carbon Steel Tubes

Carbon Steel Welded Pipe

ASTM A 106 Gr B/C Pipe & Tubes

CS Rectangular Structural Tubes

Carbon Steel Welded Tubes

Carbon Steel ERW Pipe anf Tube

API 5l carbon steel pipes

 

ASTM a106 grade A has the lowest strength of the three grades but can still be useful for many applications. A106 grade A is useful because many clients will not need a pipe that is that heavy like grade B and C so they will choose grade A because it is affordable but offers excellent quality when dealing with transporting high-temperature gases or fluids. ASTM a106 grade A can be cut or shaped to a client’s request which will be convenient for the client when using the pipe for the application needed. Grade A has the lowest amount of carbon percentage which is usually around 0.25%. This shows how the strength of the pipe is lower than the other grades.

 

 

 

Carbon Steel Seamless Pipe

Carbon Steel Tubes

Carbon Steel Welded Pipe

ASTM A 106 Gr B/C Pipe & Tubes

CS Rectangular Structural Tubes

Carbon Steel Welded Tubes

Carbon Steel ERW Pipe anf Tube

API 5l carbon steel pipes

 

ASTM A106 standard specifications

ASTM A106 is the standard specification for seamless carbon steel pipe applied for high temperature services. Dimensions Schedule Range

The standard covers pipe sizes in NPS (National Standard Straight) from 10.3mm DN6 – 1219mm DN1200 (1/8 inch to 48 inch), complied with ASME B 36.10M. But other sizes out of this B36.10 also could apply the A106 standard. Raw materials ASTM A106 standard raw material is carbon steel, it shall be applicable for bending, flanging or similar forming processes. Test Methods The test methods for the ASTM A106 A, B, C are the flattening tests, hydrostatic test, nondestructive electric test, Ultrasonic test, eddy current test, flux leakage test, these test procedures shall be notified or discussed with client to confirm what kind of test will be applied. Chemical composition in % Carbon (C) Max For Grade A 0.25, For Grade B 0.30, Grade C 0.35
Manganese (Mn): 0.27-0.93, 0.29-1.06
Sulfur (S) Max: ≤ 0.035
Phosphorus (P) : ≤ 0.035
Silicon (Si) Min : ≥0.10
Chrome (Cr): ≤ 0.40
Copper (Cu): ≤ 0.40
Molybdenum (Mo): ≤ 0.15
Nickel (Ni): ≤ 0.40
Vanadium (V): ≤ 0.08

Please note:
For each reduction of 0.01% for maximum carbon element, an increase of 0.06% manganese above the specified value shall be permitted, and up to maximum of 1.35%.
Elements Cr, Cu, Mo, Ni, V combined shall not exceed 1%.

 

 

 (1) For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.

(2)Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.

(3) These five elements combined shall not exceed 1%.

ASTM A106 standard specifications

ASTM A106 is the standard specification for seamless carbon steel pipe applied for high temperature services. Dimensions Schedule Range

The standard covers pipe sizes in NPS (National Standard Straight) from 10.3mm DN6 – 1219mm DN1200 (1/8 inch to 48 inch), complied with ASME B 36.10M. But other sizes out of this B36.10 also could apply the A106 standard. Raw materials ASTM A106 standard raw material is carbon steel, it shall be applicable for bending, flanging or similar forming processes. Test Methods The test methods for the ASTM A106 A, B, C are the flattening tests, hydrostatic test, nondestructive electric test, Ultrasonic test, eddy current test, flux leakage test, these test procedures shall be notified or discussed with client to confirm what kind of test will be applied. Chemical composition in % Carbon (C) Max For Grade A 0.25, For Grade B 0.30, Grade C 0.35
Manganese (Mn): 0.27-0.93, 0.29-1.06
Sulfur (S) Max: ≤ 0.035
Phosphorus (P) : ≤ 0.035
Silicon (Si) Min : ≥0.10
Chrome (Cr): ≤ 0.40
Copper (Cu): ≤ 0.40
Molybdenum (Mo): ≤ 0.15
Nickel (Ni): ≤ 0.40
Vanadium (V): ≤ 0.08

Please note:
For each reduction of 0.01% for maximum carbon element, an increase of 0.06% manganese above the specified value shall be permitted, and up to maximum of 1.35%.
Elements Cr, Cu, Mo, Ni, V combined shall not exceed 1%.

 

 

 (1) For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.

(2)Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.

(3) These five elements combined shall not exceed 1%.

Low temperature ASTM A333 GR. 1 Carbon Steel Line Pipe, A333 Gr.1 Welded Pipe, ASME SA333 Grade 1 Schedule 40 Pipe exporter in India

ASTM A333 grade 1 is constructed from carbon-based alloy for low temperature service. The chemical composition of the A333 carbon steel pipe includes – manganese, phosphorus and sulphur. The tensile strength and yield strength for the A333 gr b pipe is variable among its grades. For example, the tensile strength is 380 MPa and yield strength is 205 MPa for grade 1. The tensile strength is 450 MPa and yield strength is 240 MPa for grade 3. While the tensile strength is 415 MPa and yield strength is 240 MPa for ASTM A333 grade 1 pipe schedule. The pipes made from SA333 gr 1 material are meant for low temperature applications. The A333 grade 1 pipe is available in either welded, ERW, CDW, fabricated or seamless type. While producing welded pipes, it is not necessary to add filler metals during the operation. These carbon steel A333 grade 1 pipes are surface treated. The pipe ends of the A333 Gr 1 seamless pipe could be bevelled, plain ended or threaded, depending on the requirement of the buyer.

Some of the surface treatments include a coating or finishing by Oil-dip, Phosphating, Varnish, Passivation or Shot Blasting. They could also be anodized or finished polish. The treatment gives the surface of the A333 gr 1 smls pipe a smooth and flawless appearance. ASTM A333 grade 1 pipe can be conventionally formed, cold-worked and welded. The A333 grade 1 pipe can be hot worked, but they can’t be hot worked below 1500 degrees F. The ASTM A333 grade 1 pipe equivalent pipe is used in the transportation of Chemical, Water and Gas.  SA333 gr1 pipe finds application in building or construction work, where they are used to deliver concrete pumps. We are one of the oldest A333 grade 1 pipe manufacturer.

ST52 pipes come under the DIN 2391 specification. The DIN 2391 St52 Pipe is made with a chemical composition of carbon, silicon, manganese, phosphorous, and sulfur. These pipes are very strong and designed with enhanced corrosion resistance properties. DIN 2391 ST52 possesses excellent mechanical properties. They are designed with a tensile strength of minimum 600Mpa and yield strength of minimum 520Mpa. The ST52 Steel Tube can be easily elongated by a minimum of 14% and still possess good workability. They are available in single random, double random, and custom lengths up to 6000mm. ST52 Carbon Steel Pipe is produced with a carbon concentration of above 0.30%. These pipes can be easily formed by both cold and hot-rolling processes in different dimensions. The ST52 Pipe is widely used in oil and gas refineries, food processing, chemical industries, boiler systems, dairy and fluid pipelines, hydraulic systems, and so on. We are the leading ST52 Pipe suppliers in Mumbai. Our goal is to supply high-quality products at the most reasonable rates.

The ST52 Seamless Pipe is produced with the help of a billet to create a hollow shell. These pipes are extremely strong and don’t require welding or seam to join them together. The 1.0570 Steel Smls Pipe can be easily bent or flanged and can easily withstand extreme pressures and temperatures. These pipes are available with an outer diameter of 1/2NB to 60NB. The ST52 0 Seamless Tube is a mild carbon steel tube, which is extremely reliable and easy to operate. These tubes possess a smooth surface. They have a long service life and are easy to clean and maintain. DIN 1.0570 Seamless Steel Tubes is a cost-effective highly efficient pipe, which can be used in different corrosive media. These tubes are manufactured following all industry standards and are available in different shapes. The DIN2391C Seamless circular tubes are preferred in transporting and supplying fluids over long distances. These tubes are also used in different structural applications. They are very easy to maintain and clean. DIN 1629 ST 52 Plain end seamless steel tubes can be easily be connected to socket-weld connections or in slip-on flanges. These tubes create a 90-degree angle to the tube run, which makes them an ideal option in small diameter piping systems. The DIN 17100 ST 52.3 Welded Tube is produced by joining pieces of steel together. These tubes are available in pipe sizes between 5mm to 1219.2mm. All our products including, the ST52 NBK Steel pipes, can be customized in different shapes and sizes as per your requirements.

The ST52.3 Steel Cold Finished Tube is a low-carbon manganese tube. These tubes possess good impact resistance and can be readily welded. They can suffice in sub-zero temperatures and are available in normalized form. The ST52 S355 Annealed Tube is designed with excellent workability and high ductility. These tubes have low hardness and brittleness but possess good magnetic properties. In the ST52 Hydraulic Tube, the concentration of carbon is low. This grade is a preferred choice in different industries due to its excellent machinability and exceptional dimensional tolerances. The ST52 Honed Cylinder Tube possesses accurate dimensions. The abrasion resistance stones used in polishing them give them enhanced hardness and an excellent finish. ST52 4 Honed Tube can withstand extreme working pressures and temperatures. The tubes from these grades are available in normalized, phosphate finish, and oiled from the interior and exterior. The ST52-3 BK Honed Tube Tube is made with a smooth and precise finish.

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Chemical Composition of ASTM A335 Seamless Pipe:

• Carbon - 0.05% - 0.15%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.50%
• Chromium - 1.90% - 2.60.
• Molybdenum - 0.87% - 1.13%

 

 

 

 

 

 

We Yak Pipe India offers a wide range of P91 Alloy Pipe. Alloy Steel P91 Round Pipes is ductile, easy to form and weld, and possesses exceptional resistance to stress corrosion cracking in chloride – bearing solutions (a form of degradation to which the austenitic stainless steels are prone)

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P23, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P23, P91, P92

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P23, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Nominal Size: Available in 1/8-24 NB

Chemical Compositions of Alloy Steel Astm A335 Grade P23 Seamless Pipe:

 

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Nominal Size: Available in 1/8-24 NB

P9 Pipe Chemical Requirements

• Carbon - 0.15% max.
• Manganese - 0.30% - 0.60%
• Phosphorus max - 0.025%
• Sulfur max - 0.025%
• Silicon max  0.25% - 1.00%
• Chromium - 8.00% - 10.00%
• Molybdenum - 0.90% - 1.10%

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with 

A335 Gr P91 Pipes Composition StandardASTM A335 P91 Pipes Mechanical Strength Table

high quality and you can order any quantities from us. 

P91 Pipe Chemical Composition:   

• Carbon - 0.08% - 0.12%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.020%
• Sulfur, max - 0.010%
• Silicon, max – 0.20% - 0.50%
• Chromium - 8.00% - 9.50%
• Molybdenum - 0.85% - 1.05%
• Vanadium: 0.18% - 0.25%
• Nitrogen: 0.030% - 0.070%
• Nickel: 0.40% Max
• Aluminum: 0.02% Max
• Columbium: 0.06% - 0.10%
• Titanium: 0.01% Max
• Zirconium: 0.01% Max

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Chemical Composition Standard of SA335 Grade P11 Pipe A335 P11 Welded Pipes Mechanical Characteristics

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Nominal Size: Available in 1/8-24 NB

Chemical Compositions: 
Carbon - 0.05% - 0.15%

• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon – 0.50% - 1.00%
• Chromium - 1.00% - 1.50%
• Molybdenum - 0.44% - 0.65%

Mechanical Properties:

• Tensile Strength, MPa - 415 min
• Yield Strength, MPa - 205 min
• Elongation - 30 min

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.
A335 Gr P91 Pipes Composition Standard

ASTM A335 P91 Pipes Mechanical Strength Table

We are providing Alloy Steel 4130 Grade Seamless Pipes to our valuable clients.

Nominal Size: Available in 1-16 inch

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.
The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Chemical Composition Standard of SA335 Grade P11 Pipe A335 P11 Welded Pipes Mechanical Characteristics

 

 

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

P11 Pipe Chemical Requirements

• Carbon - 0.05% - 0.15%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon – 0.50% - 1.00%
• Chromium - 1.00% - 1.50%
• Molybdenum - 0.44% - 0.65%

Chemical Composition Standard of SA335 Grade P11 Pipe A335 P11 Welded Pipes Mechanical Characteristics

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

We Yak Pipe India is a renowned manufacturer, Supplier, and stockist of 4140 Grade Seamless Pipes. This pipe widespread usage all over the different industry. Grade AISI 4140 is a low alloy steel that contains additions of chromium, molybdenum, and manganese in their alloy. We provide our ASTM GR. 4140 Pipe to our clients according to the international standard. the aisi 4140 steel pipe is produced by either cold finishing or using hot finishing, which is usually cast in ingots or if required, strand cast. Once the pipe has been hot worked, it could be cold finished, and finally, they are coated with oil before being formed. Oiling the surface of ASTM A519 Grade 4140 Pipe efficiently retards the collection of dust.

Chemical Composition of Seamless grade. 4140 Pipe:

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Usage & Applications:

• Heavy Engineering Industries
• Ship Building
• Oil & Gas
• Power Plants
• Boiler Applications

 

Chemical Compositions: 

• Carbon - 0.05% - 0.15%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon – 0.50% - 1.00%
• Chromium - 1.00% - 1.50%
• Molybdenum - 0.44% - 0.65%

 

Mechanical Properties: 

• Tensile Strength, MPa - 415 min
• Yield Strength, MPa - 205 min
• Elongation - 30 min

 

Other Grades: P9/P12/P5/P9/P91

Test Certificate: Laboratory Test.

Properties:  Toughness, Strength, Hardness, Wear resistance, Hardenability, Hot hardness, Corrosion Resistance.

 

ASTM A335 Grade P5 Seamless Pipe

 

 

 

 

Chemical Composition of ASTM A335 Seamless Pipes:

• Carbon - 0.15% max
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.50%
• Chromium - 4.00% - 6.00%
• Molybdenum - 0.45% - 0.65%

Additional Information:

• Production Capacity: 20000 Kgs
• Delivery Time: 2 to 7 days
• Packaging Details: As per the client's requirement.

We are providing to our valuable clients.

Nominal Size: Available in 1-36 inch

Chemical Composition:

• Cr : 0.80-1.10% 
• Mn : 0.75-1.0%, 
• C  : 0.38-0.43% 
• Si : 0.15-0.30% 
• Mo : 0.15-0.25% 
• S  : 0.040% 
• P  : 0.035%

Specification A335 P1 is a seamless ferritic grade Alloy Steel Pipes. This specified ferritic class ASTM A335 gr P1 seamless pipes has been designed for high temperature applications. The EN 1.5415 P1 Steel Pipes material manufactured according to this specification tends to well suited for operations such as bending, flanging i.e. also referred to as vans toning as well as other similar forming operations. Additionally, the ASTM sa 335 gr P1 alloy steel pipes can be used for fusion welding. Since the alloy is occasionally referred to as P Grade, this A335 P1 Chrome Pipe is popular in several industries. This can be seen especially in the power industry as well as in Petro-chemical plants where these ferritic class based ASME SA 335 Grade P1 Alloy Steel Pipes are commonly used  in refineries.

Often, these A335 P1 pipes are known as chrome moly alloy due to the chemical makeup of these pipes including elements such as Molybdenum and Chromium. Molybdenum, when added in the alloy of ASTM A335 P1 Seamless Pipe increases the tensile strength of this chrome moly steel along with improving other properties such as its resistance to wear, elastic limit, impact qualities, and hardenability as well. While the addition of Molybdenum in the alloy of ASTM A335 P1 Pipe increases the metals resistance to softening along with restraining grain growth and making this chromium based steel less susceptible to embrittlement.  Chromium, on the other hand, when added to the seamless pipe P1 metal raises the tensile strength, yield strength, and hardness at room temperatures. Chromium is virtually irreplaceable and is known to be a very constituent of the ASTM a335 gr P1 alloy pipe since, it aids in resistance to oxidation corrosion even at elevated temperatures.

 

Standard Specification of ASTM A335 P1 Pipe

ASTM A335 P1, SA335 P1 (with IBR Test Certificate)

Size range:
1/2” NB to 36” NB

Process:
Cold rolled and Cold drawn

Schedules and thickness:
SCH 40, SCH 80, SCH 160, SCH XS, SCH XXS

Length
Standard, Custom, Cut length

Where use?
Suitable for High Temperature applications

 

ASTM A335 P22 Seamless Pipe could be used in forming operations without cracking. Bending, forging, flanging and fusion welding could be applied on this pipe. It has very high tensile strength, corrosion resistance and yield strength as well. The ASME SA 335 Grade P22 Alloy Steel Pipes could withstand high pressures and temperatures. Therefore the ASTM A335 P22 Pipe is used in applications that need to operate under high pressure and temperature. The A335 P22 Chrome Pipe has chromium in its composition which provides the high corrosion resistant properties. Also there are other elements present in the P22 steel pipe material composition. Molybdenum is a usual addition in all A335 grades. Manganese, phosphorus, silicon and carbon are added in different quantities according to the grade.

These are produced under fully annealed, isothermal annealed and normalized and tempered conditions. Since these are cold drawn, these are seamless pipes. The ASTM A335 gr P22 seamless pipe is easy to install as the dimensions are very accurate. It could be used with other a335 gr P22 alloy pipe types and fittings. The SA 335 gr P22 alloy steel pipe is highly resistant to temperature and has low thermal expansion rate. This property of the P22 metal pipe material makes it suitable for oil and gas industries, power industries, petrochemical industries and refineries where the temperatures often go high and fluctuate. The sa335 P22 seamless pipe dimensions make it suitable for welded use with pipe fittings without leakages. In high temperature and high pressure systems the pipe joints and connections are prone to cracking and leak. Since the seamless pipes have precise dimensions, these could be used with the fittings and welded for sealing of any connections. The ASTM A335 grade P22 welded pipe is a common case in many applications. 

ASTM A335 P22 Pipe Specifications Manufacturer and supplier of P22 Seamless Pipe for High-Temperature Service, check price list ex Mumbai

ASTM a106 grade A has the lowest strength of the three grades but can still be useful for many applications. A106 grade A is useful because many clients will not need a pipe that is that heavy like grade B and C so they will choose grade A because it is affordable but offers excellent quality when dealing with transporting high-temperature gases or fluids. ASTM a106 grade A can be cut or shaped to a client’s request which will be convenient for the client when using the pipe for the application needed. Grade A has the lowest amount of carbon percentage which is usually around 0.25%. This shows how the strength of the pipe is lower than the other grades.

 

 

 

Carbon Steel Seamless Pipe

Carbon Steel Tubes

Carbon Steel Welded Pipe

ASTM A 106 Gr B/C Pipe & Tubes

CS Rectangular Structural Tubes

Carbon Steel Welded Tubes

Carbon Steel ERW Pipe anf Tube

API 5l carbon steel pipes

 

ASTM A335 P91 Seamless Pipe is one of the seamless pipes of specification A335 in various industries. The ASME SA 335 Grade P91 Alloy Steel Pipes are made up of a chromium molybdenum alloy. These pipes have 1% molybdenum, 9% chromium and nickel, manganese, silicon and carbon in them. The ASTM A335 P91 Pipe has very high tensile strength, yield strength, impact cracking resistance, corrosion cracking resistance and oxidation resistance. The A335 P91 Chrome Pipe composition makes it possible for the material to have these high mechanical properties. The P91 steel pipe material could be either normalized and tempered or quenched and tempered during production. These methods add to the strength of the materials. Also, these pipes are drawn and seamless.

The ASTM A335 gr P91 seamless pipes has the advantage of possessing accurate dimensions which in turn is useful in applications that require high precision. The petrochemical industries, oil and gas industries, power generation plants and refineries often involve high temperatures and pressures. Due to the higher mechanical properties of the a335 gr P91 alloy pipes it is used widely in these industries. The SA 335 gr P91 alloy steel pipe comes in different dimensions and shapes. The wall thickness varies from 3-12 mm depending on the diameter and the pressure class of the pipes. There different schedules of the P91 metal pipes material that corresponds to different pressure classes. The sa335 P91 seamless pipes can withstand high pressure and temperature and also could be fitted with welding to other pipes and fittings. Due to the high ease of welding, the ASTM A335 grade P91 welded pipes can be welded well to make a piping system. The pipes have different tolerance levels and testing standards based on the application requirements, grades, schedules and pressure classes of the pipe material.

 

A335 P91 Pipe Specifications Finding genuine ASTM A335 p91 pipe suppliers? KNPC and Saudi Aramco approved supplier of SA335 p91 material in India

CHEMICAL REQUIREMENTS ASTM A106 [ GRADE A,B,C ] IN %

 

(1) For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.

(2)Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.

(3) These five elements combined shall not exceed 1%.

ASTM A106 standard specifications

ASTM A106 is the standard specification for seamless carbon steel pipe applied for high temperature services.

Dimensions Schedule Range

The standard covers pipe sizes in NPS (National Standard Straight) from 10.3mm DN6 – 1219mm DN1200 (1/8 inch to 48 inch), complied with ASME B 36.10M. But other sizes out of this B36.10 also could apply the A106 standard.

Raw materials

ASTM A106 standard raw material is carbon steel, it shall be applicable for bending, flanging or similar forming processes.

Test Methods

 

The test methods for the ASTM A106 A, B, C are the flattening tests, hydrostatic test, nondestructive electric test, Ultrasonic test, eddy current test, flux leakage test, these test procedures shall be notified or discussed with client to confirm what kind of test will be applied.

Alloy Steel Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in many industries for different mechanical properties such as the corrosion resistance. We are supplier of different types of alloy steel pipes. We produce and distribute the pipes of various grades, sizes and shapes. We are one of the leading Alloy Steel Pipe Manufacturer in India. There are different alloy steel available with us and the most common ones are the chromium nickel alloy pipes P1, P5, P9, P11, P12, P17, P22, P91, P92.

The Alloy Steel Seamless Pipe P1, P5, P9, P11, P12, P17, P22, P91, P92 is used in applications that require high precision for installation ease and for the accuracy of the operation and application. The different types are used for different mechanical benefits. Most of the applications require a fair amount of welding so that the welded alloy steel pipes are good for them. Some are of low strength but of high corrosion resistance and some with high strength as well. We supply the High Strength Low Alloy Steel Pipe in various grades P1, P5, P9, P11, P12, P17, P22, P91, P92 and sizes. There are different standards that govern the sizes from 1/8 inches to 60 inches and above. Our Seamless Ferrite Alloy Steel Pipe are produced with high quality and you can order any quantities from us.

Common usage & Applications:

• Gas processing equipment
• Boilers
• Petrochemical plants
• Ship-building
• Heavy Engineering Industries

Chemical Compositions:  

• Carbon - 0.08% - 0.12%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.020%
• Sulfur, max - 0.010%
• Silicon, max – 0.20% - 0.50%
• Chromium - 8.00% - 9.50%
• Molybdenum - 0.85% - 1.05%
• Vanadium: 0.18% - 0.25%
• Nitrogen: 0.030% - 0.070%
• Nickel: 0.40% Max
• Aluminum: 0.02% Max
• Columbium: 0.06% - 0.10%
• Titanium: 0.01% Max
• Zirconium: 0.01% Max

 

Physical & Mechanical Properties: 

• Tensile Strength: 415 min
• Elongation: 30 min
• Yield Strength: 205 min
• Hardness HB: 250 max

Other Details:   

• Size: 1/8" NB To 36" NB
• Types: Seamless 
• Length: 6 Meters
• Thickness: 2 mm To 15 mm 
• Schedule: SCH 20, SCH 40, SCH 80, SCH 160, SCH XS, SCH XXS, All Schedules.
• Outside Coating: As per the client's requirements.

ASTM A106 standard specifications

ASTM A106 is the standard specification for seamless carbon steel pipe applied for high temperature services.

Dimensions Schedule Range

The standard covers pipe sizes in NPS (National Standard Straight) from 10.3mm DN6 – 1219mm DN1200 (1/8 inch to 48 inch), complied with ASME B 36.10M. But other sizes out of this B36.10 also could apply the A106 standard.

CHEMICAL REQUIREMENTS ASTM A106 [ GRADE A,B,C ] IN %

 

(1) For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.

(2)Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.

(3) These five elements combined shall not exceed 1%.

We Yak Pipe India are providing Nickel Alloy Pipes to our valuable clients.

Chemical Composition:

• C - 0.3% max
• Cu - 28-34% max
• Fe - 2.5% max
• Mn - 2.0% max
• Ni - 63.0% min
• S  - 0.024% max
• Si - 0.5% max

S355 is a non-alloy European standard (EN 10025-2) structural steel, most commonly used after S235 where more strength is needed. It got great weld ability and machinability, let us see more mechanical details of this steel.

S355 Yield Strength

S355 is named based on it's minimum yield strength of 355 Mpa (N/mm2), However the yield strength reduces when you go up in thickness above 16 mm for flat products & hollow sections

Here is the table showing reduction in yield strength based on thickness
Up to 16 mm - 355 Mpa
16 mm < t  ≤ 40 mm -  345 Mpa
40 mm < t  ≤ 63 mm -  335 Mpa
63 mm < t  ≤ 80 mm -  325 Mpa
80 mm < t  ≤ 100 mm -  315 Mpa
100 mm < t  ≤ 150 mm -  295 Mpa

S355 Tensile Strength

S355 ultimate tensile strength ranges also varies based on thickness.
Up to 3 mm - 510 Mpa to 680 Mpa
3 mm < t  ≤ 100 mm -  470 Mpa to 630 Mpa
100 mm < t  ≤ 150 mm -  450 Mpa to 600 Mpa

S355 Density

Density of S355 is 7850 kg/m3 like all other mild steel

S355 Hardness (Brinell Hardness - HB)

Hardness for S355 J2 ranges from 146 HB to 187 HB

S355 Young's Modulus S355 Youngs's Modulus is 190 to 210 Gpa, in a conservative design go for 190 Gpa